1.4889(GX40NiCrNb45-35)炉管、炉辊、耐热钢铸件

1.4889(GX40NiCrNb45-35)属于欧标耐热钢，执行标准：EN 10295-2002

1.4889(GX40NiCrNb45-35)化学成分及机械性能如下图：

Mechanical properties

ReHMinimum yield strength / Mindestwert der oberen Streckgrenze / Limite d elasticite minimale

RmTensile strength / Zugfestigkeit / Resistance a la traction

AMinimum elongation / Mindestwert der Bruchdehnung / Allongement minimal

JNotch impact test / Kerbschlagbiegeversuch / Essai de flexion par choc

Heat treatment conditions

+ASoft annealed+ACAnnealed to achieve spheroidization of the carbides

+ARAs rolled+ATSolution annealed

+CCold drawn / hard+CRCold rolled+FPTreated to ferrite-pearlite structure and hardness range

+IIsothermal annealing+LCCold drawn / soft

+MThermo mechanical rolling+NNormalized

+NTNormalized and tempered+PPrecipitation hardened

+PEPeeled+QAAir quenched and tempered

+QLLiquid quenched and tempered+QTQuenched and tempered

+STreated to improve shearability+SHAs rolled and turned

+SRCold drawn and stress relieved

耐热钢是指具有高温抗氧化性和高温强度的钢。高温抗氧化性是保证工件在高温下持久工作的重要条件。钢件在高温空气等氧化环境中，氧与钢表面发生化学反应生成多种铁的氧化物层，该氧化物层很疏松，失去了钢的原有特性，极易脱落。为了提高钢的高温抗氧化性，向钢中加入合金元素，从而改变氧化物的结构。常用的合金元素有铬、硅、铝等。它们与氧反应，在钢的表面上生成致密的、稳定的氧化物层，或者说钝化层Cr2O3、SiO2或者Al2O3等，以保护钢不再继续氧化。铬、硅、铝加入量多，钢的高温抗氧化好，但是若硅、铝加入量太多，钢的力学性能和工艺性变差。所以，耐热钢以铬为主要合金元素，以硅、铝为辅助元素，总之，钢的高温抗氧化性只与化学成分有关。

1. 工业领域：在钢铁、有色金属、石化和玻璃等工业领域，耐热钢炉辊是必不可少的设备之一。在钢铁工业中，炉辊用于高炉、转炉、电炉等设备，支撑和传递熔融金属和矿石。在有色金属行业，炉辊主要用于铜冶炼、铝冶炼等生产过程中的熔炼和传输。在石化行业，炉辊应用于炼油和化工生产中的加热、熔化和混合等工艺。在玻璃行业，炉辊则是玻璃制品生产中的重要设备之一‌。

2.建筑领域：在建筑领域，耐热钢炉辊主要应用于水泥生产过程中的煅烧工艺。水泥烧成需要高温和长时间的煅烧过程，炉辊作为支撑和传递热量的设备，起到了关键作用。此外，炉辊还应用于玻璃生产和陶瓷制造等行业中‌。

3.交通领域：在交通运输领域，耐热钢炉辊主要应用于铁路车辆制造，用于热处理和热成形工艺。此外，炉辊还应用于汽车制造和飞机制造等行业中，确保材料的连续传输和处理‌。